| Customization: | Available |
|---|---|
| Game: | Tennis |
| Thickness: | 3mm-10mm |
|
Still deciding? Get samples of US$ 2/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Excellent Performance
1·Buffering effect given by res ilience protects the athletes' joints and reduces sport injury.
2·The surface layer of acrylic cushion provides certain protection to accidental falls in sports.
3·The tennis court with buffering effect has a longer sport life.
4·The resilient tennis courts provide more stable ball speed and ball direction. The sport felling is better.
5·The surface layer of the acrylic cushion tennis court provides more comfortable sporting texture when athletes are starting, stopping abruptly or sliding.
| Pavement materials | Base requirements | Competition performance | Environmental performance | Durability | Usage limits |
| SPU material | Both cement and asphalt base | The hard upper and resilient under structure is special for tennis. The low modulus cushion layer at the bottom plays the most appropriate buffer effect. The high modulus strengthen layer in the middle provides sufficient compression rebound. The tenacity hard surface provides superior sport texture. The whole system ensures the tennis court has effective buffer, slip resistance to starting, moving and rebound performance. | Environmental. The product implements strictly the latest State Mandatory Standards of Indoor Decorating and Renovating Material and qualified in 'China Environmental Label(type I) by China's Ministry of Environmental Protection |
The base coat and the cushion layer is airtight to isolate the underground moisture and prevent bubbling. The high extensibility prevent the tiny crack caused by deformation of the cement base. The surface is wearable, scratch-resistant, and uvioresistan. It is non-aging, color lasting and not easy to sand-out. Renovations, changing color or line are convenient. | It is suitable for both indoor and outdoor and not affected by any climate in principle. After rain, it just needs to clean the water on the surface and then put into use. |
| The traditional acrylic material | Asphalt base only | The new tennis courts have good sport texture in early stage. It is comfortable to start and the friction is stable. But the buffer absorption effect is bad. It has low resilience and lacks enough sport protection. The old one gets to harden and easy to cause injury to the athletes' joints. The sand consolidation effectiveness is worse. It sand-out easily and get to be smooth. | Environmental, odorless and non-toxic | Water resistance is not good. Low strength durability. Easy to sand-out. Low color durability. Need roll-coating renovation frequently to keep competition performance. The base material has low strengthen and easy to aging and harden. It is easy to conduct cracks on the surface. The low-priced products blend much more filler. Quality and performance change apparently. | Suitable for both indoor and outdoor. Dark soles are easy to produce friction marks on the surface. It is not easy to clear. Only if it is dry thoroughly can put into use. Otherwise, it is easy to damage the site. |
| NO. | Items | Index of standard | Results |
| value of rebound, % | ≥80 | 88 | |
| impact absorption | 5~15 | 9 | |
| Slid friction, N | 60~100 | 76 | |
| Water permeability, mm/min | 0 | 0 |
| NO. | Items | Index of standard | Results | |
| 1 | Tensile elongation, % | ≥400 | 857 | |
| 2 | tensile strength, MPa | ≥1.8 | 3.2 | |
| 3 | artificial weathering ageing resistance d(300h) | No bubble, no peeling, no crack; Powder ≤grade 1, △E≤5.0 | No bubble, no peeling, no crack; Powder ≤grade 1, △E=0.9 | |
| 4 | Durability, aging test (168h) | Tensile elongation, % | ≥300 | 858 |
| tensile strength, MPa | ≥1.3 | 1.6 | ||
| 5 | wearability(750g/500r)/g | ≤0.050 | 0.035 | |
| 6 | water resistance |
No bubble, no peeling, allows slight discoloration, recover after 2h | No bubble, no peeling, no discoloration | |
| 7 | Flame retardancy, class | I | I | |